Affordable Hydrogen Fuel Production Using Surface Reconstruction Strategy

The hydrogen evolution reaction (HER) is a remarkable process that can create clean hydrogen fuel - a potential part of a solution to our climate change crisis. The problem lies in scaling up this reaction from a lab experiment to large scale commercial production, while keeping costs down.

The findings were published in Advanced Energy Materials on April 3, 2025.

In their search for superior HER performance, researchers at Tohoku University demonstrated that a surface reconstruction pathway can produce durable non-noble metal-based cathodes that speed up the HER reaction. They can maintain their performance for more than 300 hours and are calculated to cost very close to the US Department of Energy's 2026 H₂ production target ($2.00 per kg_H2^-1). This could pave the way for the rational design of brand new, highly-efficient non-noble metal-based cathodes for commercial PEM application - finally bridging the gap from laboratory to factory.

The angle this study approached for trying to improve the HER - which tends to be inefficient and slow by nature - was transition metal phosphides (TMPs). This promising catalyst (which improves the HER's efficiency) is a durable and cost-effective non-noble metal. However, typically noble metals are used, so the researchers recognized that there was a knowledge gap about non-noble metals that needed to be filled.

The research team prepared F modified CoP and examined aspects such as its surface reconstruction and true active sites using operando X-ray absorption spectroscopy (XAS) and Raman measurements. Essentially, adding the F in the CoP_1-x lattice allows for P-vacancy sites to form on the surface, which leads to more active sites that are able to speed up the HER.

"This reconstructed Co is highly active, works in acidic conditions, and can maintain approximately 76 W for over 300 hours," says Heng Liu (Advanced Institute for Materials Research (WPI-AIMR)). "We're getting close to an affordable method to produce fuel. The calculated cost of using this method is $2.17 per kg_H2^-1 - just 17 cents over the current production target set for 2026."

The researchers found that when this F modified CoP cathode underwent surface reconstruction, its activity was improved. The experiment doesn't just test the setup in a lab-scale experimental setup with three electrodes, but also extends the findings to commercial-scale PEM electrolyzers. These results are significant advancements in HER catalyst research that could be the basis for the rational design of other non-noble metal-based cathodes.

"We're always thinking about the end goal, which is for research to make its way into everyday life. This advancement brings us one step closer to designing more realistic options for commercial PEM application," says Liu.

https://www.tohoku.ac.jp/en/press/affordable_hydrogen_fuel_production_using_surface_reconstruction_strategy.html

Title: Surface Reconstruction Activates Non-Noble Metal Cathode for Proton Exchange Membrane Water Electrolyzer
Authors: Rui Wu, Heng Liu, Jie Xu, Ming-Rong Qu, You-Yi Qin, Xu-Sheng Zheng, Jun-Fa Zhu, Hao Li, Xiao-Zhi Su, Shu-Hong Yu
Journal: Advanced Energy Materials
DOI: https://doi.org/10.1002/aenm.202405846

Attached files

Characterizations of CoP|F-20 and CoP. a) Schematic synthetic illustration of CoP|F on CFP. b) SEM image of CoP|F-20 nanosheets on a single carbon fiber. Scale bar, 2 µm. c) A false-color TEM image of a typical CoP|F-20 nanosheet, showing its relative thickness. Scale bar, 100 nm. d) Atomic-resolution STEM images of CoP|F-20. Scale bar, 1 nm. Inset up right shows the corresponding FFT pattern, and down left shows crystal structure along [101̄] zone axis. e STEM-EDX elemental mapping of CoP|F-20, showing the homogeneous distribution of Co (green), P (blue), and F (red). Scale bar, 200 nm. HAADF-STEM images of CoP|F-20 f and CoP g, and corresponding integrated pixel intensities h of spacings along (201) facet. Scale bar, 1 nm. i) Co 2p and j) P 2p XPS spectra of CoP|F-20 and CoP catalysts. k XANES spectra at Co K-edge of CoP|F-20, CoP, and Co foil. l) R-space curve-fitting of EXAFS spectra of CoP|F-20 and CoP. ©Heng Liu et al.
Theoretical calculations on the electrochemistry-induced P-vacancy formation (Pv) and HER activity. a-c) Calculated surface Pourbaix diagrams for a) CoP(010), b) CoP|F(010) with 1F doped at the subsurface, and c) CoP|F(010) with 2F doped at the subsurface. The term ∆∆G refers to the difference in Gibbs free energy between the pristine system and the system after the formation of a phosphorus vacancy. d) The identified surfaces with 1 monolayer Pv formation. Blue, purple, and red spheres represent P, Co, and F, respectively. e) HER volcano activity model showing the theoretical activities of the CoP|F(010) surfaces with Pv. ©Heng Liu et al.
PEM test of CoP|F-20 catalyst. a) Schematic illustration of a PEM cell. b) I-V curves of PEM electrolyzers using commercial IrO2 as an anodic catalyst and CoP|F-20 as a cathodic catalyst. No cell voltages were iR compensated. c) Time-dependent power and total H2 generation of PEM electrolyzers using commercial IrO2 as an anodic catalyst and CoP|F-20 as a cathodic catalyst at 1 A cm-2. ©Heng Liu et al.

25/04/2025 Tohoku University

Regions: Asia, Japan

Keywords: Science, Chemistry, Physics

Disclaimer: AlphaGalileo is not responsible for the accuracy of content posted to AlphaGalileo by contributing institutions or for the use of any information through the AlphaGalileo system.

Latest Publications

Testimonials